Comparative study of physical-chemical properties of bioactive glass ionomer cement

Abstract This study analyzed the physical-chemical properties of bioactive ionomer materials. Cention N bioactive materials were evaluated chemically activated (CN) and light-cured (CN-LC), Equia Forte Fill (EQUI); conventional resin composite Filtek Z350 XT (Z350); resin glass ionomer cement Riva light Cure (RIVA) and flowable resin composite Filtek Bulk Fill Flow (BULK-F) were evaluated. Sixty specimens (n=10) were prepared for sorption (SR), solubility (SL), flexural strength (FS), shrinkage stress (SS), conversion degree (CD), microhardness (MI), and surface roughness (SR) tests. Non-cured and light-cured materials were assessed on FTIR. 30 human molar teeth were used in the bond strength test (BS). Data were subjected to ANOVA and post-hoc Tukey's test (5% of significance). EQUI showed more sorption in SR and no statistical difference from RIVA and CN-LC. CN group showed more solubility and EQUI presented less (p<0.05). BULK-F showed higher FS (MPa), without differences from CN and Z350, whereas EQUI presented the lowest FS not differing from RIVA. BULK-F and CN-LC showed more shrinkage stress differing from EQUI. CN-LC and CN showed higher CD differing from the other which showed no differences (p>0.05) between them. EQUI showed the highest hardness (p<0.05) in MI. There were no differences (p>0.05) in SR (µm). Z350 and BULK-F presented higher BS, whereas CN-LC showed the lowest, although not differing from EQUI and RIVA. Equia Forte's solubility and microhardness make it a good alternative as a restorative material. Cention N degree of conversion and flexural strength making it an esthetic option to amalgam.

Resumo Este estudo analisou as propriedades físico-químicas dos materiais de ionômero bioativo. Os materiais bioativos Cention N quimicamente ativados (CN) e fotopolimerizados (CN-LC), Equia Forte Fill (EQUI); resina composta convencional Filtek Z350 XT (Z350); resina de ionômero de vidro Riva light Cure (RIVA) e resina composta fluida Filtek Bulk Fill Flow (BULK-F) foram avaliados. Sessenta espécimes (n=10) foram preparados para testes de sorção (SR), solubilidade (SL), resistência à flexão (FS), tensão de contração (SS), grau de conversão (CD), microdureza (MI) e rugosidade da superfície (SR). Os materiais não curados e curados com luz foram avaliados por FTIR. 30 dentes molares humanos foram usados no teste de resistência de união (BS). Os dados foram submetidos a ANOVA e teste de post-hoc Tukey (5% de significância). O EQUI apresentou maior sorção no SR e não mostrou diferença estatística em relação aos grupos RIVA e CN-LC. O grupo CN apresentou maior solubilidade e o EQUI apresentou menor (p<0,05). O BULK-F apresentou maior FS (MPa), sem diferir do CN e do Z350, enquanto o EQUI apresentou o menor FS, não diferindo do RIVA. O BULK-F e o CN-LC apresentaram maior estresse de contração, diferindo do EQUI. O CN-LC e o CN apresentaram maior CD (%), diferindo dos demais, que não apresentaram diferenças (p>0,05) entre si. A EQUI apresentou a maior dureza (p<0,05) no MI. Não houve diferenças (p>0,05) na SR (µm). Z350 and BULK-F apresentaram BS, enquanto a CN-LC apresentou a menor, embora não diferindo da EQUI e da RIVA. A solubilidade e a microdureza do Equia Forte o tornam uma boa alternativa como material restaurador. O grau de conversão e a resistência à flexão do Cention N o tornam uma opção estética ao amálgama.

Insertion methods and gap/void formation in atraumatic restorative technique: A micro-CT analysis

Abstract Wetting the dentin is critical to atraumatic restorative treatment. The conventional insertion can be challenging when using high-viscosity glass-ionomer cement. This study evaluated the formation of gaps and voids after three insertion methods using micro-CT. Teeth underwent removal of occlusal and proximal caries through the atraumatic restorative treatment technique. Then, they were fixed in an artificial dental arch to simulate the clinical condition and were restored using three insertion methods: conventional, Centrix injection, and double-filling. Previous dentin conditioning procedures, steel matrix and wooden wedge application, and post-insertion procedures (digital compression and surface protection) were the same. The material was inserted using a manual instrument in the conventional technique and was inserted with a syringe in the Centrix injection group. In the double-filling technique, the tooth received a first layer of a flowable ionomer (through modifying the powder/liquid ratio), and a second layer (with standard ratio) was applied before the final set of the first one. A micro-CT unit scanned each tooth before and after restoration. Each cavity was defined as the volume of interest, and the volumes of gaps and voids were calculated. Data were analyzed using one-way ANOVA and Tukey posthoc test (p < .05). Double-filling had improved filling volume with lower values for gap volume, followed by Centrix injection. The conventional technique had the highest gap volume. No statistically significant difference was observed for void volume. Double-filling demonstrated fewer gaps, followed by Centrix injection, which is critical to obtain better adhesive, remineralizing, and antibacterial activities.

Resumo O molhamento da dentina parcialmente desmineralizada no fundo da cavidade dentária é fundamental para o sucesso do tratamento restaurador atraumático. No entanto, o método de inserção convencional pode ser desafiador ao usar cimento de ionômero de vidro de alta viscosidade. Este estudo avaliou a formação de gaps e vazios internos após três métodos de inserção de cimento de ionômero de vidro de alta viscosidade usando micro-CT. Dez terceiros molares foram submetidos à remoção de cárie oclusal através da técnica de tratamento restaurador atraumático e complementação proximal (com ou sem lesão pré-existente). Em seguida, foram fixados em uma arcada dentária artificial para simular a condição clínica. Os dentes foram restaurados usando a técnica de tratamento restaurador atraumático com três métodos de inserção: convencional, injeção Centrix e dupla inserção. Os procedimentos anteriores de condicionamento dentinário, inserção de matriz de aço, aplicação de cunha de madeira e procedimentos pós-inserção do material (como compressão digital e proteção de superfície) foram os mesmos para os três grupos testados. O material foi inserido com instrumento manual na técnica convencional, seguindo a metodologia clássica do tratamento restaurador atraumático. O material foi inserido com um dispositivo desenvolvido especificamente para esse fim na técnica de inserção com seringa tipo Centrix. Na técnica de dupla obturação, o dente recebeu uma primeira camada do cimento de ionômero de vidro mais fluido (obtido através da modificação da relação pó/líquido), e uma segunda camada (com relação pó/líquido padrão) foi aplicada antes da presa final da primeira. Um micro-CT escaneou cada dente antes e depois da restauração. Cada cavidade foi definida como o volume de interesse, e os volumes de gaps e vazios foram calculados. Os dados foram analisados por ANOVA one-way e teste post-hoc de Tukey com nível de significância de 5%. A dupla inserção melhorou significativamente o volume de preenchimento com valores percentuais mais baixos para o volume do gap, seguido pela injeção com seringa tipo Centrix. A técnica convencional apresentou o maior percentual de volume de gap. Nenhuma diferença estatisticamente significativa foi observada para o volume de vazios internos. O grupo de dupla inserção demonstrou menor formação de gaps, seguido pelo grupo de injeção com seringa tipo Centrix, que é fundamental para obter melhores atividades adesivas, remineralizantes e antibacterianas.

Effect of aging and cementation systems on the bond strength to root dentin after fiber post cementation

Abstract This study evaluated the effect of aging and cementation of fiber posts using glass ionomer and resin cements on push-out bond strength, failure mode, and resin tag formation. One hundred and twenty bovine incisors were used. After post-space preparation, the specimens were randomly allocated into 12 groups (n = 10) according to the cementation system used: GC - GC Gold Label Luting & Lining); RL - RelyX Luting 2; MC - MaxCem Elite; RU - RelyX U200 and the aging periods (24 hours, 6 months, and 12 months). Slices from the cervical, middle, and apical thirds were obtained and analyzed by push-out bond strength test and confocal laser scanning microscopy. One-way ANOVA and Tukey's post-hoc test was used at a significance level of 5%. For the push-out bond strength test, no differences among GC, RU, and MC in the cervical and middle thirds were observed, regardless of the period of storage (P > 0.05). In the apical third, GC and RU showed similar bond strength but higher than other groups (P > 0.05). After 12 months, GC showed the highest bond strength (P < 0.05). Bond strength to post-space dentin decreased over time, regardless of the cementation system used. Cohesive failure was the most frequent, regardless of the period of storage, cementation system, and post-space third. Tag formation was similar among all groups. After 12 months, GC showed the highest bond strength values.

Resumo Avaliar o efeito do envelhecimento e sistemas de cimentação usando ionômero de vidro e cimentos resinosos na resistência de união à dentina após a cimentação do pino de fibra. Cento e vinte incisivos bovinos foram utilizados. Após o preparo do pós-espaço, os corpos de prova foram distribuídos aleatoriamente em 12 grupos (n = 10) de acordo com o período de envelhecimento (24 horas, 6 meses e 12 meses) e o sistema de cimentação utilizado: GC - cimento de ionômero de vidro (GC Gold Label Cimentação e Revestimento); RL - RelyX Luting 2; MC - MaxCem Elite; RU - RelyX U200. Cortes dos terços cervical, médio e apical foram obtidos e analisados por teste de resistência de união push-out e microscopia confocal de varredura a laser. ANOVA one-way e teste de Tukey foi usado a um nível de significância de 5%. Para o teste de resistência de união, não foram observadas diferenças entre GC, RU e MC nos terços cervical e médio, independentemente do período de armazenamento (P > 0,05). No terço apical, GC e RU apresentaram resistência de união semelhante, porém superior aos demais grupos (P > 0,05). Após 12 meses, o GC apresentou a maior resistência de união (P < 0,05). A resistência de união à dentina no espaço para pino diminuiu ao longo do tempo, independentemente do sistema de cimentação utilizado. A formação de tags foi semelhante entre todos os grupos. Após 12 meses, o GC apresentou os maiores valores de resistência de união.

Research progress on fluoride-releasing restorative materials for caries control / 口腔疾病防治

@#Restorative materials such as conventional glass ionomer cement (CGIC), resin-modified glass ionomer cement (RMGIC), polyacid-modified composite resin (compomer), and giomer have the properties of fluoride release and refill, which may prevent or slow down the progression of caries. The caries resistance of these materials was evaluated according to the following criteria: fluorine-releasing ability, antibacterial activity, mechanical properties and anti-aging properties. The anti-caries effect of these materials mainly depends on the effect of fluoride ions on mineralization. However, materials with strong fluorine release ability, such as CGIC, are mainly used in pediatric dentistry and temporary restoration due to their poor mechanical properties. It is difficult to achieve both fluoride ion release potential and mechanical strength, and there are few materials that can provide ideal mechanical strength while maintaining a high standard of fluoride release. The fluoride releasing and recharging capacity of CGIC, RMGIC, compomer and giomer decrease successively. The trend of material modification, to a certain extent, tends to sacrifice the fluoride release capacity of materials to maintain the ideal mechanical strength. In recent years, scholars have tried to add a variety of fillers to further enhance the anti-cracking ability of materials and add antibacterial agents to compensate for the anti-caries effect to reduce the loss of fluoride release.

Influence of paper mixing pads thickness on the compressive strength of glass ionomer cement / 北京大学学报(医学版)

OBJECTIVE@#To explore the influence of the thickness of mixed cardboard on the compressive strength of glass ionomer cement and the associated factors.@*METHODS@#Three different types of glass ionomer cements were mixed on the top of 60, 40, 20 and 1 pieces of paper (P60, P40, P20 and P1), respectively. The compressive strength of the materials was tested after solidification, and the bubble rate was calculated with the assistance of scanning electron microscope.@*RESULTS@#(1) Compressive strength: ① ChemFil Superior glass ionomer (CF): The average compressive strength of P1 group was the highest, which was significantly different from that of P40 and P60 groups (P values were 0.041 and 0.032 respectively); ② To Fuji IX GP glass ionomer (IX): The average compressive strength of P1 group was the highest, which was statistically different from that of P40 and P60 groups (P values were 0.042 and 0.038 respectively); ③ Glaslonomer FX-Ⅱ glass ionomer cement (FX): The average compressive strength of P1 group was the highest, which was statistically different from that of P20, P40 and P60 groups (P values were 0.031, 0.040 and 0.041 respectively), but there was no statistical difference among the other groups. All the three materials showed that the compressive strength of glass ions gradually increased with the decrease of the thickness of the blended paperboard, and the two materials had a highly linear negative correlation, the correlation coefficients of which were CF-0.927, IX-0.989, FX-0.892, respectively. (2) Scanning electron microscope: P1 group had the least bubbles among the three materials.@*CONCLUSION@#It indicates that the thickness of mixed cardboard has a negative correlation with the compressive strength of glass ions. The thicker the mixed cardboard is, the greater the elasticity is. Excessive elasticity will accelerate the mixing speed when the grinding glass ions. Studies have shown that the faster the speed of artificial mixing is, the more bubbles is produced.The thicker ther mixed cardboard is, the more bubblesn are generated by glass ionomer cement, and the higher the compressive strength is. Using one piece of paper board to mix glass ionomer cement has the least bubbles and can obtain higher compressive strength.

Investigation of the effect of indirect pulp capping materials on dentin mineral density

Aim: To evaluate the potential of inducing mineral density changes of indirect pulp capping materials applied to demineralized dentin. Methods: A total of 50 cavities were prepared, 5 in each tooth, in extracted ten molars without caries, impacted or semi-embedded. The cavities were scanned by microcomputed tomography (µ-CT) after creating artificial caries by microcosm method (pre-treatment). Each cavity was subjected to one of 5 different experimental conditions: control (dental wax), conventional glass ionomer cement (Fuji IX GP Extra), resin-modified calcium silicate (TheraCal LC), resin-modified calcium hydroxide (Ultra-Blend Plus), MTA (MM-MTA) and the samples were kept under intrapulpal pressure using simulated body fluid for 45 days. Then, the second µ-CT scan was performed (post-treatment), and the change in dentin mineral density was calculated. Afterward, elemental mapping was performed on the dentinal surfaces adjacent to the pulp capping agents of 5 randomly selected samples using energy dispersive X-ray spectroscopy (EDS) apparatus attached to a scanning electron microscope (SEM). The Ca/P ratio by weight was calculated. Friedman test and Wilcoxon Signed Ranks test were used to analyze the data. Results: There was a significant increase in mineral density values of demineralized dentin after treatment for all material groups (p<0.05). Resin-modified calcium silicate had similar efficacy to MTA and conventional glass ionomer cement, but was superior to resin-modified calcium hydroxide in increasing the mineral density values of demineralized dentin. Conclusions: Demineralized dentin tissue that is still repairable can be effectively preserved using materials with remineralization capability

Randomized controlled trial on the effectiveness of silver diamine fluoride in arresting caries in Lagos, Nigeria

Treatment of dental caries in children still remains challenging due to lack of cooperation with conventional treatment modalities. Recently, the use of Silver Diamine Fluoride (SDF) has proved useful in addressing this challenge. Aim: This clinical trial aimed to evaluate the effectiveness of Silver Diamine Fluoride (SDF) in arresting caries in children in Lagos, Nigeria. Methods: This was a phase III balanced randomized controlled school based interventional study on 240 children. The study group was treated with SDF while GIC was used in the control group. Follow up visits in 2 weeks, 1 month, and 3 months were carried out to assess the treatment outcome. Inferential statistics with the use of Pearson Chi-square test and Independent Student t-test were used at 5% level of significance. Results: There was significant relationship between SDF and caries arrest in 2 weeks, 1 month and 3 months' assessment period (p = 0.001). The control group showed continuous decline (71.7%, 54.3% and 50.9%) in restorative success from 2 weeks to 3 months respectively. The mean ± SD and Confidence Interval (CI) of arrested caries in the SDF group were 113± 1.24 and 113.1 ­ 113.5 respectively. In the control group the mean ± SD and CI of restorative success were 69.3±11.8 and 67.2 ­ 71.4. The effect size was 5.24. Conclusion: The result of the study showed that SDF was effective in arresting caries in children without any harm and there was statistically significant difference in the use of 38% SDF in arresting caries in children

Reconstruction of the Long Process of the Incus by Use of Glass Ionomer Cement: Our Experience

Abstract Introduction Chronic suppurative otitis media is one of the most common causes of reversible conductive hearing loss which can lead to necrosis of the ossicles. The incus, especially its long process, is the most common ossicle affected. Objectives The present study aims to assess the use of glass ionomer cement for the reconstruction of the long process of the incus. Methods The present study was conducted on 27 patients with chronic suppurative otitis media with central perforation with dry and quiescent ears with an eroded long process of the incus submitted to tympanoplasty. The audiological evaluations were done on all patients, including preoperative and postoperative evaluation of the airbone gap; the average pure tone threshold was done 6 months postoperatively. Results The average air pure tone threshold was 42.8 dB preoperatively and 22.5 dB postoperatively. The postoperative air pure tone thresholds were significantly smaller than the preoperative values (p < 0.01). The air-bone gap was 30.5 dB at 500 Hz, 31.6 dB at 1 KHz, and 24.1 dB at 2 kHz preoperatively, and 7.7 dB at 500 Hz, 7.2 dB at 1 KHz, and 7.1 dB at 2 kHz postoperatively at the end of 6 months of follow-up. There were significant hearing gains in the air-bone gap (p < 0.001). Conclusion Glass ionomer cement is a useful and effective material for bridging the defect of the long process of the incus.

Evaluation and comparison of silorane resin composite to glass ionomer in occluso-proximal restorations of primary molars A randomized controlled trial

Objective: In general, proximal restorations of primary molars fracture, so it is vital to study the new materials that could solve this problem. Hence, the present trial assessed the success of occluso-proximal atraumatic restorative treatment (ART) restorations using silorane and glass ionomer cement (GIC) in carious primary molars for a period of 2 years. Materials and Methods: One hundred and ninety-two children between the age group of 4 and 9 years were randomly allocated to GIC or silorane. In the clinical set up, they were treated by a pediatric dentist, and their restorations were evaluated at 3, 6, 12, 18, and 24 months. The primary outcome was the survival of restoration, which was analyzed using the Kaplan–Meier and superior Cox regression models. As a sensitivity analysis, intention-to-treat (ITT) was executed. Sex, age, molar, jaw, cavity volume, and caries incidence were the independent variables. Results: The restoration survival after 24 months for GIC and silorane was 82.75% and 88.88%, respectively, whereas ITT analysis showed a success of 84.37% and 89.58% for GIC and silorane, respectively. Conclusion: With regard to longevity, there was no statistically significant difference between silorane and GIC in primary molar occlusoproximal ART restorations.

Anti-Bacterial Effect, Fluoride Release, and Compressive Strength of a Glass ionomer Containing Silver and Titanium Nanoparticles

Background: Many attempts have been made to enhance the anti?cariogenic properties of the conventional glass ionomer through incorporation of variable materials. However, most importantly, the incorporation of such materials should not jeopardise the physical or mechanical properties of the final restoration. Aims: To investigate the effect of adding silver nanoparticles (Ag?NPs) and titanium dioxide nanoparticles (TiO2?NPs) to conventional glass ionomer cement (GIC) on its anti?bacterial effect against Streptococcus mutans (S. mutans), fluoride ion release, and compressive strength (CS). Settings and Design: This study was an in vitro investigation where 30?disc specimens were prepared in each of the three studied groups. Materials and Methods: The specimens were categorized into the control group (Group C), in which conventional GIC was used, and Group Ag and Group Ti, in which 5 wt% of Ag?NP and TiO2?NP were added, respectively, to GIC powder. In each group, the anti?bacterial effect against S. mutans, fluoride ion release at 24 hours and 14 and 28 days, and CS were assessed. Data were analysed using one?way analysis of variance, followed by Tukey honest significant difference post?hoc test. Results: Both Ag and Ti groups showed a significantly higher anti?bacterial effect than the control group. Ag?NP increased fluoride ion release, whereas TiO2?NP decreased fluoride release; however, cumulative ion release of both experimental groups did not differ significantly compared to the control group. Adding Ag?NP and TiO2?NP increased CS, yet only the Ti group showed the highest CS mean value that was statistically significant compared to other groups. Conclusions: Adding 5 wt% TiO2?NP or Ag?NP to conventional GIC significantly increased its anti?bacterial effect and its CS without affecting fluoride release.

In vivo evaluation of clinical performance of Cention N and glass ionomer cement in proximal restorations of primary molars

Introduction: Restoring a proximal lesion in primary tooth has met with many challenges which has led to evolution of many materials. An alternative to Glass Ionomer Cements which has fluoride releasing capacity, offers good bond strength and is esthetic have been long looked for. Aim: This study aimed to compare the clinical performance of GIC and Cention N in proximal restorations of primary molars. Materials and Methodology: A prospective study was conducted on 154 primary molars in patients aged between 5 and 8 years using a split-mouth design. Patients were divided into two groups. Control group restored with GIC and study group received Cention N. Both groups were assessed at baseline 3, 6 and 9 months according to Ryge criteria and data was statistically analysed using Fisher's Exact. Results: Statistically significant difference was found between GIC and Cention N restorations for color match at baseline and color stability at 3 months (P < 0.001), while the other parameters did not show any significant difference among the two restorative materials. Conclusion: Cention N can be used as a suitable alternative to GIC for restoring Class II restorations in primary molars.

Effect of silver diamine fluoride, potassium iodide, and glutathione on micro-shear bond strength of glass ionomer cement to caries affected dentine

Background: Silver diamine fluoride (SDF, 38%) is an efficient topical fluoride used to arrest dental caries though it causes black staining of both teeth and restoration. The application of potassium iodide (KI) after SDF reduces the stain, but the color change is only temporary. An alternative method suggested is by mixing glutathione (GSH) with SDF, which preserves the silver ions of SDF within the solution. Hence, the purpose of this in vitro study was to evaluate the microshear bond strength (?SBS) of glass ionomer cement (GIC) to caries affected dentin (CAD) pretreated with SDF/KI/GSH. Materials and Methods: Thirty dentine slices of 2 mm thickness from human permanent upper premolars were demineralized using pH cycling method to mimic CAD. They were allocated to three groups of 10 each and treated with SDF, SDF-KI (SDF followed by KI), SDF + GSH (SDF mixed with GSH), respectively. Specimens were bonded with GICs. The ?SBS was assessed using a universal testing machine and the data obtained were analyzed using one-way ANOVA and Tukey's post hoc test. Results: The ?SBS (mean ± standard deviation) values for groups SDF, SDF-KI, and SDF + GSH were 4.81 ± 2.026, 5.78 ± 1.809, 8.18 ± 2.828 megapascal respectively. Group 3 showed significantly better bond strength compared to groups 1 and 2. In group 2, the addition of KI showed better bond strength when compared to group 1, but the difference was not statistically significant. Conclusion: Pretreatment of teeth with GSH along with SDF application showed significantly better bond strength of GIC to CAD compared to SDF and SDF-KI.

ART restorations for occluso-proximal cavities in primary molars: a two-year survival and cost analysis of an RCT comparing two GIC brands

Abstract There are many glass ionomer cements available on the Brazilian market for Atraumatic Restorative Treatment (ART), however, there is still a gap in the literature regarding their cost-effectiveness. Objectives To evaluate the influence of restorative materials (Ketac Molar, 3M ESPE; and Vitro Molar, Nova DFL) in the two-year survival rate and cost-effectiveness of occluso-proximal ART restorations in primary molars. Methodology A total of 117 children (aged four to eight years) with at least one occluso-proximal carious lesion in primary molars were selected and randomly divided in treatment groups (KM or VM) in this parallel randomized controlled trial. Treatments followed ART premises and were conducted in public schools by trained operators in Barueri, Brazil. A trained, calibrated, and blinded examiner performed the evaluations after two, six, 12, and 24 months (k=0.92). Kaplan-Meier survival analysis was used to estimate restoration survival and Cox regression was used to test the association with clinical factors (α=5%). For cost analysis, material and professional costs were considered. Monte Carlo analysis was used to generate a cost-effectiveness plane and bootstrapping was used to compare material costs over the years. Results The overall survival rate was 36.9% after two years (48.6% for KM and 25.4% for VM). Restorations with VM failed more than those with KM (HR=1.70; 95% CI=1.06-2.73; p=0.027). VM presented lower initial cost, but no difference was observed between groups considering the two-year incremental cost. Conclusion After a two-year evaluation, KM proved to be a better option than VM for occluso-proximal ART restorations in primary molars. ClinicalTrials.gov: NCT02267720

Release characterization and biological effect of Glass Ionomer Functionalized with two different chlorohexidine derivatives: an in vitro study

ABSTRACT Objective: To evaluate the effect of adding two different chlorohexidine derivatives; chlorhexidine hexametaphosphate and chlorhexidine digluconate to glass ionomer at three different concentrations (0.25%, 0.75%and 1.5%) regarding the antibacterial effect, chlorhexidine release and fluoride release. Methods: A total of 405 specimens were prepared and tested after 7 days, 3 months and 6 months of storage in distilled water (n=5).For testing antibacterial effect, chlorhexidine release and fluoride release, the mix was packed in a ready-made Split Teflon molds to obtain disc-shaped specimen with dimensions 10 mm in diameter and 2 mm thickness according to ISO standardizations. One-way ANOVA and One-way repeated measure ANOVA test were used for statistical analysis of data. Results: The incorporation of chlorhexidine into ChemFil Superior glass ionomer cement in both derivatives has high significance ability to provide a long-term antimicrobial effect on Streptococcus mutans and Lactobacillius acidophilus. The chlorhexidine release was increased by adding chlorhexidine in both derivatives to GIC than the unmodified Glass-ionomer cement for study duration. However, the fluoride release was decreased in the modified specimens than the original one. Conclusion: Addition of chlorhexidine enhanced the antibacterial effect of the glass ionomer and chlorhexidine release. However, fluoride release was reduced than original

Effect of delayed light-curing on solubility, color stability, and opacity of Fuji II LC glass ionomer cement: original article / Efeito da fotopolimerização tardia na solubilidade, estabilidade de cor e opacidade do cimento de ionômero de vidro Fuji II LC: artigo original

Objective: Resin-modified glass ionomer (RMGI) cements are among the commonly used restorative materials in low stress-bearing areas and also for temporary restorations. The competition between acid-base reactions and light polymerization reactions in delayed curing of RMGIs can affect their physical and mechanical properties, as well as their degree of conversion. Since solubility, color stability, and opacity are among the main physical properties affecting the durability and clinical service of RMGI restorations, this study aimed to assess the effect of delayed curing on solubility, color stability, and opacity of Fuji II LC RMGI. Material and Methods: This in vitro, experimental study evaluated 80 Fuji II LC RMGI specimens (10 specimens per each in 4 groups) in terms of solubility, color stability, and opacity at 6 months later. Specimens were cured immediately or were cured with 1, 5 and 10 min delay. Results: Maximum solubility and minimum change in opacity and color stability at 6 months were noted in the group with delayed curing by 10 min. A significant difference was noted in the solubility of specimens cured after 10 min and 1 min. Significant differences were also noted in the opacity and color stability of specimens cured after 10 min and all other groups (P < 0.05). Conclusion: Delayed curing by 1 min decreased the solubility of RMGI specimens compared with immediate curing or curing after 5 min. Although this difference did not reach statistical significance. Color stability and changes in opacity are mainly influenced by the acid-base reactions rather than polymerization reactions.(AU)

Objetivo: Cimentos de ionômero de vidro modificado por resina (CIVMR) estão entre os materiais restauradores mais comumente utilizados em áreas de baixa tensão e também para restaurações temporárias. A competição entre reações ácido-base e reações provenientes da fotopolimerização tardia dos CIVRMs podem afetar suas propriedades físicas e mecânicas, bem como seu grau de conversão. Uma vez que a solubilidade, estabilidade de cor e opacidade estão entre as principais propriedades físicas que afetam a durabilidade e o tempo de serviço clinico de restaurações de CIVMR, este estudo teve como objetivo avaliar o efeito da fotopolimerizaçao tardia na solubilidade, estabilidade de cor e opacidade do CIVMR Fuji II LC. Material e Métodos: Este estudo experimental in vitro avaliou 80 espécimes de CIVMR Fuji II LC (4 grupos com 10 espécimes cada) em termos de solubilidade, estabilidade de cor e opacidade apos 6 meses. As amostras foram fotopolimerizadas imediatamente ou com 1, 5 e 10 min de atraso. Resultados: Máxima solubilidade e mínima alteração na opacidade e estabilidade da cor em 6 meses foram observadas no grupo com fotopolimerização tardia em 10 min. Uma diferença significativa foi observada na solubilidade das amostras fotopolimerizadas após 10 min e 1 min. Diferenças significativas também foram observadas na opacidade e estabilidade de cor das amostras fotopolimerizadas após 10 min e em todos os outros grupos (P <0,05). Conclusão: A fotopolimerizaçao tardia em 1 min diminuiu a solubilidade das amostras CIVMR em comparação com a fotopolimerizaçao imediata ou após 5 min. Embora essa diferença não tenha alcançado significância estatística. A estabilidade da cor e as mudanças na opacidade são influenciadas principalmente por reações ácido-base, em vez de reações causadas pela polimerização(AU)

Research progress on natural antibacterial ingredients of glass ionomer cement / 口腔疾病防治

@#Glass ionomer cement (GIC) is widely used as a common filling material in dentistry but still exhibits problems with secondary caries and fractures. Thus, the antibacterial and anti-caries performance of GIC needs to be further improved. In recent years, natural antimicrobial components have become more desirable due to their good biological properties and low drug resistance. In this review, the natural antimicrobial ingredients in GIC modification are classified, reviewed and summarized according to the different sources of antimicrobial ingredients. In terms of animal origin, chitosan and casein phosphopeptide-amorphous calcium phosphate exhibit antimicrobial properties without affecting the mechanical properties of materials; propolis and bioactive enzymes have good biocompatibility; in terms of plant origin, polyphenols help improve the antimicrobial and mechanical properties of the material; arginine has a good remineralization effect; and plant essential oils have a certain ion release effect. In terms of microbial origin, antibiotics greatly improve the antibacterial properties of materials; in addition, the combined application of natural antimicrobial ingredients also exhibited excellent performance. Despite these advantages, the optimal addition concentration and biocompatibility in vivo are questions that need to be further explored before clinical applications can be achieved.

Propiedades y aplicación clínica de los ionómeros de vidrio de alta densidad disponibles en Lima-Perú / Properties and clinical application of high density glass ionomers available in Lima-Peru

El objetivo de la revisión fue conocer las propiedades y la aplicación clínica de los diferentes ionómeros de vidrio de alta densidad disponibles en Lima-Perú. Se realizó una revisión de la literatura científica desde enero 2010 hasta diciembre 2019 acerca de los ionómeros de vidrio de alta densidad. Esta revisión se realizó en las bases de datos SciELO, Pubmed y Google Scholar. Los descriptores para realizar la búsqueda fueron: cementos de ionómero de vidrio, ionómeros de vidrio de alta densidad y propiedades físicas, las combinaciones entre ellos y su equivalente en inglés. Se seleccionaron finalmente 40 artículos que cumplieron con los criterios de inclusión. Dentro de las marcas de ionómeros de alta densidad disponibles en Lima-Perú se encuentran: Ionofil® Plus (VOCO), KetacTM Molar Easymix (3M ESPE), Fuji IX GP (GC corporation) y EQUIA Forte™®GC (Europe GC). Se presentan las propiedades y aplicación clínica de todos estos ionómeros. De acuerdo a la revisión de la literatura, de los cinco grupos estudiados: EQUIA Forte presentó una excelente adhesión al esmalte y la dentina. Fuji IX GP puede ser usado en restauraciones de Clase I y II, sin contactos oclusales y; EQUIA Forte puede utilizarse en pequeñas Clase II con /sin contactos oclusales, y con cuidado en grandes cavidades MOD siguiendo las recomendaciones del fabricante.

The objective of the review was to understand the properties and clinical application of the different high-density glass ionomers available in Lima, Perú. A review of the scientific literature about high-density glass ionomers, was conducted from January 2010 to December 2019. This review was performed in SciELO, Pubmed and Google Scholar databases. The descriptors used in the search were: glass ionomer cements, high density glass ionomers and physical properties, the combinations between them and their equivalent in English. Ultimately forty articles that met the inclusion criteria, were selected. The high-density ionomers available in Lima-Peru are Ionofil® Plus (VOCO), KetacTM Molar Easymix (3M ESPE), Fuji IX GP (GC corporation) and EQUIA Forte™® GC (Europe GC). The properties and clinical application of all these ionomers are presented. According to the literature review, of the five groups studied; EQUIA Forte presented excellent adhesion to enamel and dentin. Fuji IX GP can be placed in Class II restorations without occlusal contacts and EQUIA Forte can be used in small Class II with / without occlusal contacts, and cautiously in large MOD cavities following the manufacturer's recommendations.

Effect of handpiece light and material used in pulp chamber on dentin removal during root canal retreatment

Abstract This study evaluated the effect of the use of glass ionomer cement (GIC) and flowable bulk-fill resin composite (BFRC) for filling pulp chambers and the type of high-speed handpiece light used on dentin removal during access preparation for endodontic retreatment in molar teeth. Twenty maxillary molars were treated endodontically. BFRC (Opus Bulk Fill Flow APS, FGM) was used to fill the pulp chamber and replace coronal dentin (n = 10). In the remaining teeth, the pulp chamber was filled with GIC (Maxion R, FGM). Conventional resin composite (Opallis, FGM) was used to restore the enamel layer in all teeth. The samples in each group were divided into two subgroups, and the root canals were reaccessed using a handpiece with white or ultraviolet light. The teeth were scanned using micro-CT before and after root canal reaccess. The dentin volume removed was calculated and analyzed using 2-way analysis of variance and Tukey's test (α = 0.05). The crown and pulp chamber locations with dentin removal are described using frequency distribution. During the access, fewer pulp chamber walls were affected and a lower volume of dentin was removed from the pulpal floor in the group restored with GIC than in the group restored with BFRC. No effect was observed on the coronal dentin walls with respect to the filling protocols and type of light used. For dentin removal from the pulp chamber, handpieces with white light performed better than those with ultraviolet light, irrespective of the filling protocol used. The use of GIC to fill the pulp chamber and use of white handpiece light reduced dentin removal from the pulpal floor and resulted in fewer affected dentin walls.

Resumo Este estudo avaliou os efeitos do cimento de ionômero de vidro (GIC) e da resina composta fluida bulk fill (BFRC) usados como preenchimento da câmara pulpar; e o tipo de iluminação das turbinas de alta rotação na remoção dentinária após cavidades de acesso para retratamento endodôntico em dentes molares. Vinte molares superiores foram tratados endodonticamente. Dez dentes foram restaurados usando BFRC (Opus Bulk Fill Flow APS, FGM) para preencher a câmara pulpar e dentina coronária; e resina composta convencional (Opallis, FGM) para restaurar a camada de esmalte. Os outros dentes foram restaurados usando GIC (Maxion R, FGM) para preencher a câmara pulpar e resina composta (Opallis, FGM). As amostras foram divididas em dois grupos e os canais radiculares foram novamente acessados com turbina de alta-rotação com iluminação branca ou ultravioleta. Os dentes foram escaneados usando micro-CT antes e após o novo acesso ao canal radicular. O volume de dentina removida foi calculado e os dados foram analisados por ANOVA bidirecional e teste de Tukey (α=0,05). As regiões na coroa e na câmara pulpar que apresentaram dentina removida no acesso dos canais foram descritas por meio de distribuição por frequência. A reabertura do canal radicular com GIC resultou em menos paredes afetadas da câmara pulpar e menor volume de dentina removida no assoalho. Nenhum efeito foi observado nas paredes de dentina coronária considerando aos protocolos de preenchimento. A turbina de alta rotação com iluminação branca reduziu a remoção de dentina da câmara pulpar, independentemente do protocolo de restauração utilizado. O uso de turbina de alta rotação com iluminação branca e GIC para preencher a câmara pulpar reduziram a remoção de dentina do assoalho e afetaram menos paredes dentinárias.

Efeito de dentifrício com alta concentração de flúor na remineralização e resistência de união de cimento de ionômero de vidro em substratos dentários com cárie artificial / Effect of dentifrice with high concentration of fluoride under remineralization and bond strength of glass ionomer cement on dental substrates with artificial caries

O objetivo do presente estudo foi avaliar a influência de diferentes dentifrícios na dureza de superfície, em secção transversal e perfil de desgaste do esmalte, assim como na resistência de união de cimentos de ionômero de vidro de alta viscosidade (CIV-AV) à dentina, após indução de cárie artificial, ciclagem de pH e escovação. Foram utilizados 80 dentes bovinos, divididos em blocos de esmalte e dentina. Os espécimes de esmalte foram polidos e selecionados de acordo com a microdureza. Em seguida, metade de cada bloco de esmalte foi protegida com verniz ácido resistente. Os espécimes de dentina foram incluídos em resina acrílica e planificados. O protocolo de cárie artificial foi feito através de ciclos de desmineralização em esmalte (n=20) e pela imersão da dentina (n=40) em solução desmineralizadora. Vinte amostras de dentina não foram submetidas à cárie, sendo o grupo controle. Todas as amostras foram submetidas à ciclagem de pH e escovação durante 7 dias de acordo com cada dentifrício: Colgate Total 12 1450 ppm F (CT) e Clinpro 5000 ppm F + TCP (CL). Em seguida, os blocos de esmalte foram submetidos às análises de dureza de superfície, em secção transversal e perfilometria. Microscopia eletrônica de varredura foi realizada em três blocos representativos de cada grupo. Os espécimes de dentina foram subdivididos de acordo com material restaurador: CIV-AV Ketac Molar (KM) e cimento ionomérico híbrido Equia Forte (EF). Em seguida, as amostras foram armazenadas sob umidade relativa durante 24 horas e preparados para o teste de microcisalhamento. Os dados obtidos foram submetidos ao teste de normalidade, análise de variância (ANOVA) 1 critério para avaliar a recuperação mineral e perfil de desgaste, ANOVA 2 critérios com medidas repetidas para avaliar a dureza de superfície e em secção transversal, ANOVA 3 critérios para avaliar o microcisalhamento e pós teste de Tukey para comparações múltiplas, com significância de 5%. Observou-se recuperação parcial da dureza de superfície, independente do dentifrício. Os dados da dureza em secção transversal evidenciaram que CL obteve valores inferiores a CT até 90 micrômetros (m) no lado teste. O dentifrício CT apresentou maior desgaste quando comparado à CL. Em dentina, ao comparar os dentifrícios dentro de cada CIV, CT apresentou maior resistência adesiva para ambos os materiais. A comparação entre CIVs dentro do mesmo dentifrício evidenciou resistência adesiva superior para KM quando comparado à EF na dentina tratada com CL. Conclui-se que o dentifrício com maior concentração de flúor promoveu menor dureza em secção transversal no esmalte e o dentifrício convencional resultou em maior desgaste superficial. Na superfície dentinária, o dentifrício com maior concentração de flúor diminuiu a resistência adesiva de cimentos de ionômero de vidro(AU)

The aim of the present study was to evaluate the influence of different dentifrices on surface hardness and cross-sectional hardness, wear profile on enamel, as well as on the bond strength of high viscosity glass ionomer cements (HV-GIC) to dentin, after to produce artificial caries, pH cycling and brushing. Eighty bovine teeth were used, divided into enamel and dentin blocks. The enamel specimens were polished and selected according to microhardness. Then, half of each enamel block was covered with resistant acid varnish. Dentin specimens were embedded in acrylic resin and flattened. The artificial caries protocol was carried out through enamel demineralization cycles (n= 20), and the dentin (n= 40) was immersed in demineralizing solution. Twenty dentin specimens were not subjected to artificial caries, being the control group. All blocks were subjected to pH cycling and brushing for 7 days according to each dentifrice: Colgate Total 12 1450 ppm F (CT) and Clinpro 5000 ppm F + TCP (CL). Then, the protected enamel surfaces were exposed for the analysis of surface hardness, cross sectional hardness and profilometry. Scanning electron microscopy was performed in three representative blocks of each group. The dentin specimens were subdivided according to restorative material: HVGIC Ketac Molar (KM), and hybrid GIC Equia Forte (EF). Then, the specimens were stored under relative humidity for 24 hours and prepared for the micro-shear test. The data were submitted to normality test, one-way analysis of variance (ANOVA) to assess mineral recovery and wear, two-way repeated measures ANOVA to assess surface and cross-sectional hardness, and three-way ANOVA to analyze the bond strength. Tukey post-test was used for multiple comparisons, with a significance level of 5%. It was observed a partial recovery of superficial microhardness, regardless of the dentifrice. Cross sectional hardness data showed that CL obtained values below CT up to 90 micrometers (m) on the test side. CT dentifrice presented greater wear when compared to CL. In dentin, when the dentifrices were compared within each GIC, CT showed greater adhesive resistance for both materials. A comparison between GICs within the same dentifrice showed superior adhesive resistance for KM when compared to EF in dentin treated with CL. It was concluded that the dentifrice with the highest fluoride concentration promoted less cross-sectional hardness in the enamel and the conventional dentifrice resulted in greater surface wear. On the dentin, the dentifrice with the highest fluoride concentration decreased the adhesive strength of glass ionomer cements(AU)

Effect of the polishing procedure and surface sealant application on fluoride release / Efeito do procedimento de polimento e aplicação superficial de selante na liberação de flúor

Objectives: This study aimed to assess the effect of the polishing procedure and surface sealant application on the fluoride release of restorative materials. Material and Methods: The groups were consisted of using five different restorative materials were employed: Beautifil II, GCP Glass Fill, Amalgomer CR, Zirconomer and Fuji IX GP. 30 disk-shaped specimens (8x2 mm) were prepared from each material. Each group was subdivided into three groups considering finishing procedures: Mylar strip, polishing with Super-Snap discs, G-Coat Plus application after polishing with Super-Snap discs. The amount of fluoride released into distilled water was measured using a fluoride ion-selective electrode and ion analyzer after 24 hours, followed by measurement on days 3, 7, 15, 21, and 28. Surface analysis of the materials was performed with SEM (Scanning Electron Microscopy) and EDS (Energy Dispersive X-ray Spectroscopy). The data were statistically analyzed using two-way repeated measure ANOVA and LSD test (p=0.05). Results: The highest amount of fluoride released was measured after the first 24 h for all materials. Beautifil II released less fluoride than other materials in all measurement periods (p<0.05). After polishing, the amount of fluoride released from all materials except Beautifil II increased (p<0.05). The application of G-Coat Plus did not impact the amount of fluoride release of any materials (p>0.05). EDS analysis showed the most percentage of oxygen in all materials. Conclusion: The polishing procedure might induce an increase in fluoride release of glass ionomer-based materials, and the application of G-Coat Plus cannot affect the amount of fluoride release. (AU)

Objetivos: Este estudo teve como objetivo avaliar o efeito do procedimento de polimento e aplicação de selante superficial na liberação de flúor de materiais restauradores. Material e Métodos: Os grupos consistiram na utilização de cinco materiais restauradores diferentes: Beautifil II, GCP Glass Fill, Amalgomer CR, Zirconomer e Fuji IX GP. Trinta espécimes em forma de disco (8x2 mm) foram preparados a partir de cada material. Cada grupo foi subdividido em três grupos considerando os procedimentos de acabamento: tira Mylar, polimento com discos Super-Snap, aplicação de G-Coat Plus após polimento com discos Super-Snap. A quantidade de flúor liberada na água destilada foi medida usando um eletrodo íon-seletivo de fluoreto e analisador de íons após 24 horas, seguido pela medição nos dias 3, 7, 15, 21 e 28. A análise da superfície dos materiais foi realizada com MEV (Microscopia Eletrônica de Varredura) e EDS (Espectroscopia de Energia Dispersiva de Raios-X). Os dados foram analisados estatisticamente usando ANOVA de dois fatores com medidas repetidas e teste LSD (p = 0,05). Resultados: A maior quantidade de flúor liberado foi medida após as primeiras 24 horas para todos os materiais. O Beautifil II liberou menos flúor do que outros materiais em todos os períodos avaliados (p <0,05). Após o polimento, a quantidade de flúor liberada de todos os materiais, exceto Beautifil II, aumentou (p <0,05). A aplicação de G-Coat Plus não afetou a quantidade de liberação de flúor de nenhum material (p> 0,05). A análise por EDS revelou a maior porcentagem de oxigênio em todos os materiais. Conclusão: O procedimento de polimento pode induzir um aumento na liberação de flúor de materiais à base de ionômero de vidro, e a aplicação de G-Coat Plus não pode afetar a quantidade de liberação de flúor (AU)